Comprehensive analysis of the performance of welding joints of gas pipelines with different viscosities
DOI:
https://doi.org/10.32347/2410-2547.2023.111.276-283Keywords:
pipe, deformation, crack, plastic zone, polygonAbstract
Full-scale tests of gas pipelines with different viscosities were carried out in landfill conditions, which are as close as possible to the natural conditions of operation of gas pipelines. The kinetics of crack propagation along welded joints - their trajectory, the transition from the weld seam to the base metal of the pipe and vice versa, the speed of movement of cracks in viscous and brittle metal and defined zones of plastic deformation - were experimentally investigated. It is known that tests on Menaget, Charpy and other samples, which have thicknesses that do not correspond to the thickness of the pipe walls, do not reflect the real picture of visco-plastic and brittle fractures, which does not allow to develop a methodology or model for predicting the final resource (non-accident) of long-term gas pipelines period of operation. At the same time, theoretical and laboratory researches do not always adequately answer the questions directly related to ensuring the durability and trouble-free operation of pipelines. It is likely that in the laboratory conditions of enterprises or scientific institutions it is difficult to reproduce and take into account all the factors that characterize the growth and spread of destruction in a real operating gas pipeline. Therefore, the data of laboratory studies must be checked and necessarily clarified according to the results of pneumatic tests of long pipe sections, i.e., at present, the need to combine laboratory and field tests of pipes of the gas pipeline network is urgently needed. Such tests are not massive, but as a result of their performance, important information is obtained regarding the behavior and properties of the metal in the conditions of loading and operation, which are closest to operational conditions. In field tests, pipes with a diameter of 1000x18 mm were used, which underwent controlled rolling (steel class X70 - grade 06G2BA) at a working pressure of RR = 9.7 MPa (in the northern - low-temperature version). Tensile tests, studies of impact toughness, strength and plasticity of the weld metal were carried out according to standard methods described in works [2-5]. During the experiments, a large number of sensors of temperature, pressure, strain, stress, crack propagation speed, etc. were used. The obtained results regarding the kinetics of the destruction of natural pipes in landfill conditions lay the groundwork for the development of a mathematical model of the engineering forecast of the residual (non-accident) resource of pipelines operating in oil and gas fields.
References
Andreykiv O.E., Nikyforchyn H.M., Tkachev B.I. Mitsnist i ruinuvannia metalichnykh materialiv i elementiv konstruktsii u vodnevomisnykh seredovyshchakh (Strength and destruction of metallic materials and structural elements in hydrogen-containing environments) // Physical and Mechanical Institute: - Ed. V.V. Panasyuka, NAS of Ukraine, Institute of Physics and Mechanics named after G.V. Karpenka - Lviv: Prostir-M, 2001. - 248-286 p.
Vasylenko I.I., Melekhov R.K. Koroziine roztriskuvannia stalei (Corrosion cracking of steels) - Kyiv: Nauk, dumka, 1977. - 265 p.
Dmytrykh I.M., Panasiuk V.V. Vplyv koroziinykh seredovyshch na lokalne ruinuvannia metaliv bilia kontsentpatopiv napruzhen (The influence of corrosive environments on the local destruction of metals near stress concentrators) - Lviv: Lviv regional book printing house, 1999. - 342 p.
Kryzhanivskyi E.I., Tsirulnyk O.T., Petryna D.Yu. Vplyv navodniuvannia ta poperednoho plastychnoho deformuvannia stali na yii trishchynostiikist (The influence of water treatment and preliminary plastic deformation of steel on its crack resistance) // Phys.-chem. mechanics of materials. - 1999. - No. 5. - 67-70 p.
Radkevich O.I., Pyasetskyi O.C., Vasylenko I.I. Koroziino-mekhanichna tryvkist trubnoi staliv sirkovodnevomu seredovyshchi (Corrosion-mechanical durability of pipe steel in a hydrogen sulfide environment)// Phys.-chem. mechanics of materials. -2000. - No. 3. - 93-97 p.
Standart NACE TM01-77(90). Standartnyi metod testuvannia. Laboratorne vyprobuvannia stiikosti metaliv do sulfidnoho roztriskuvannia v seredovyshchi H2S (NACE Standard TM01-77(90). Standard Test Method. Laboratory Testing of Metals Resistance to Sulfide Stress Cracking in H2S Environments) // NACE. - Houston. P.O. BOX 218340. 1990.-22 p.
Okada T., Hattori S. Spivvidnoshennia mizh kontsentratsiieiu solonoi vody ta koroziinoiu vtomnoiu mitsnistiu 0,37% vuhletsevoi konstruktsiinoi stali (Relation Between Concentration of Salt Water and Corrosion Fatique Strength on 0.37 Percent Carbon Structural Steel) Fukui University, Japan: Theoretical foundations of engineering calculations (Proceedings of the American Society of Mechanical Engineers)// Myr publishing house, 1985, No. 3, 98-107p.
Tkachev V.I. Problemy vodnevoi dehradatsii metaliv (Problems of hydrogen degradation of metals)// Phys.-chem. mechanics of materials. -2000.-№4.—7-14 p.
Borysova N.C., Amosova L.M. Do pytannia pro anomalnu povedinku vodniu v staliakh za nyzkykh temperatur (To the question of anomalous behavior of hydrogen in steels at low temperatures)// Phys.-chem. mechanics of materials. - Lviv. -1986.-№12.-10-13 p.
Panasyuk V.V., Andreykiv A.E., Harin V.S. Model zrostannia trishchyn u deformovanykh metalakh pry dii vodniu (A model of crack growth in deformed metals under the influence of hydrogen)// Phys.-chem. mechanics of materials.-1987.-№2.-3-17 p.
Shvachko V.I. Mikromekhanichni aspekty oborotnoi vodnevoi krykhkosti (Macromechanical aspects of reversible hydrogen embrittlement)// Phys.-chem. mechanics of materials. -2000.- No. 4.-36-40 p.
Makarenko V.D., Kryzhanivskyi E.I., Chernov V.Yu. Problemy koroziinoi stiikosti promyslovykh truboprovodiv (Problems of corrosion resistance of industrial pipelines// Oil and gas industry). -2002.-№6.-42-44p
Samoilenko M.I. Funktsionalna nadiinist truboprovidnykh transportnykh system (Functional reliability of pipeline transport systems)// Kharkiv: KhNAMP. – 2009.-184 p.
Nasonina N.G., Antonenko S.E. Analiz poshkodzhenosti vodoprovidnykh i kanalizatsiinykh merezh (Damage analysis of water supply and sewage networks// Modern industrial and civil construction) -2019.-Vol.15.-No.1.- 23-34 p.
Makarenko V.D., Gots V.I., Argatenko T.V. etc. Doslidzhennia avariinykh truboprovodiv// Problemy vodopostachannia, vodovidvedennia ta hidravliky (Research of emergency pipelines// Problems of water supply, drainage and hydraulics)//vol. 42. -2023.- 49-58 p.
Brydu A., Lafrance M., Provu I. Rozrobka novykh sortiv stali z pidvyshchenymy kharakterystykamy dlia transportuvannia kysloho hazu ta nafty (Development of new grades of steel with increased characteristics for the transport of sour gas and oil)// Neftegaz-France – Yuzychor Asye, 1986. -19 p.
A.I. Radkevich, R.K. Melekhov, Y.I. Spektor, R.V. Yatsenko Doslidzhennia vitchyznianykh ta zarubizhnykh nyzkolehovanykh sirkovodoroldostiikykh stalei dlia naftohazoprovidnoho obladnannia (Research of domestic and foreign low-alloy hydrogen sulfide-resistant steels for oil and gas pipeline equipment) // Mezhotraslevaya nauch-conf. Structural steel - progressive production processes and efficiency of application. Dnipropetrovsk, 1995. - 58-59 p.
Vasylenko I.I., Shulte O.Yu., Radkevich O.I. Vplyv khimichnoho skladu i tekhnolohii vyrobnytstva stalei na yikh chutlyvist do vodnevoho trishchyno utvorennia ta sirkovodnevoho koroziinoho roztriskuvannia (The influence of the chemical composition and production technology of steels on their sensitivity to hydrogen cracking and hydrogen sulfide corrosion cracking)// Physic-chemical mechanics of materials. -1990.-№4.-8-22 p.
O. Chaplya, O. Radkevich, O. Pyasetskyi, Ya. Cpektor Porivnialnyi analiz koroziino-mekhanichnykh vlastyvostei vitchyznianoi trubnoi stali 20YuCh z inozemnymy analohamy (Comparative analysis of corrosion-mechanical properties of domestic pipe steel 20ХХ with foreign analogues) //Mashinoznavstvo. -1999.-№8.- 52-56p
20. O. Radkevich, G. Chumalo, I. Dominyuk and others. Osnovni zakonomirnosti navodniuvannia ta poverkhnevoho pukhyrinnia trubno'i stali v sirkovodnevykh seredovyshchakh (Basic regularities of waterlogging and surface blistering of pipe steel in hydrogen sulfide environments) // Phys.-chem. mechanics of materials. - 2004. - Special. issue No. 4, vol. 1. - 446-449 p.
Tyson W.R. Vodneve okrykhchennia ta vodnevi dyslokatsiini vzaiemodii (Hydrogen Embrittlement and Hydrogen Dislocation Interactions )// Corrosion. - 1980. Vol. 36, No. 8. -441-443 p.
22. YuYa Meshkov. Fizychni osnovy ruinuvannia stalevykh konstruktsii (Physical foundations of the destruction of steel structures)// Kyiv Scientific opinion 1981 – 265 p.
Ford F.P. Koroziine roztriskuvannia pid napruhoiu v rozvytku korozii (Stress Corrosion Cracking in Advances in Corrosions) Science -1, Ed., R.N.Parkins, Applied Science Publishers, 2002.
Kawakubo T, Hisida M. Rozrakhunok pryskorenoho navkolyshnim seredovyshchem rostu trishchyny dlia neirzhaviiuchoi stali u vodi vysokoi temperatury na osnovi mekhaniky pruzhno-plastychnoho ruinuvannia (Calculation of environmentally accelerated crack growth for stainless steel in high-temperature water based on elastic-plastic fracture mechanics)//Journal of Engineering Materials and Technology, 1995, Vol.107, 240-245p
Makarenko V.D. Eksperymentalni vyprobuvannia truboprovodiv (Experimental tests of pipelines)//Nizhyn: Mykola Gogol State University, 2020.-543 p.
Makarenko V.D., Stognii O.V., Gots V.I. etc. Polihonni vyprobuvannia hazoprovodiv (Polygon tests of gas pipelines) Monograph// Nizhin: NSU named after M. Gogol. -2023. - 160 p.
Downloads
Published
Issue
Section
License
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.